♦CPVC-C5212-O
NO | ITEM | UNIT | STANDARD | TEST METHOD |
1 | Appearance | Granules | ||
2 | Specific Gravity | g/cm3 | 1.47-1.49 | GB/T1033.1-2008 |
3 | Performance density | g/ml | 0.60-0.62 | GB/T20022-2005 |
4 | Volatile content ≤ | wt % | 0.3 | GB/T2914-2008 |
5 | Vicat Softening Temp ≥ | ℃ | 102 | GB/T1633-2000 |
6 | Tensile Strength ≥ | MPa | 50 | GB/T1040.2-2006 |
7 | Tensile Modulus Of Elasticity ≥ | MPa | 2488 | GB/T1040.2-2006 |
8 | Elongation ≥ | % | 30 | GB/T1040.2-2006 |
9 | Impact Strength(Izod)≥ | KJ/m2 | 14 | GB/T1043.1-2008 |
10 | Dynamic Thermal Stabilization Time ≥ | min | 25 |
ADVANTAGES:
♦CPVC-C5212-O
NO | ITEM | UNIT | STANDARD | TEST METHOD |
1 | Appearance | Granules | ||
2 | Specific Gravity | g/cm3 | 1.47-1.49 | GB/T1033.1-2008 |
3 | Performance density | g/ml | 0.60-0.62 | GB/T20022-2005 |
4 | Volatile content ≤ | wt % | 0.3 | GB/T2914-2008 |
5 | Vicat Softening Temp ≥ | ℃ | 102 | GB/T1633-2000 |
6 | Tensile Strength ≥ | MPa | 50 | GB/T1040.2-2006 |
7 | Tensile Modulus Of Elasticity ≥ | MPa | 2488 | GB/T1040.2-2006 |
8 | Elongation ≥ | % | 30 | GB/T1040.2-2006 |
9 | Impact Strength(Izod)≥ | KJ/m2 | 14 | GB/T1043.1-2008 |
10 | Dynamic Thermal Stabilization Time ≥ | min | 25 |